Chung Metal produces Aluminium 2014 forgings for demanding applications where utmost strength is a necessity. Being a high-strength aluminum-copper alloy, 2014 boasts superior machinability and fatigue life, suitable for heavy-duty structural parts. Our accuracy in forging process ensures improved grain flow and less internal defect, leading to better mechanical properties and reliability. Forgings are heat-treated according to customer specifications, providing consistent performance in aerospace, transportation, and heavy engineering industries where optimum strength and durability are a priority.
Aluminium 2014 is usually composed of 4.4% copper, 0.8–1.2% silicon, 0.5–1.0% manganese, and traces of magnesium, iron, and minor trace elements. It is heat treatable and has high tensile strength of 460–500 MPa, yield strength of 300–400 MPa, and elongation of 8–12%. Hardness is around 120–135 HB in T6 condition. Although corrosion resistance is not very high, it can be enhanced by the application of coatings or cladding. Good machining and response to mechanical stress.
Standards : ASTM B247, B247
Temper : T6 T651 T6511
Specification : DIN, ASTM, BS and all International Standards
Flat bar blocks : up to 27″ width and 15,000 lbs.
Cylinders and sleeves : up to 50″ maximum O.D. and 65″ maximum length
Discs and hubs : up to 50″ diameter and 20,000 lbs.
Rolled, hand forged or mandrel forged rings : up to 84″ maximum O.D. and 40″ maximum length
Rounds, shafts and step shafts : up to 144″ maximum length and 20,000 lbs.
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 – 1.20 | 0.2 – 0.8 | 0.4 – 1.2 | 3.9 – 5.0 | 0.25 | 0.15 | 93.5 |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| STANDARD | UNS | WERKSTOFF NR. | European Standard | BS (OLD) | ISO | USA (AA) | GERMANY (DIN) | IS | Canadian |
| Aluminium 2014 | A92014 | 3.1255 | EN AW-2014 | HE15 | AlCu4SiMg | 2014 | AlCuSiMn | 24345 | B26S |
Yes, Aluminum 2014 is suitable for high-temperature forging applications due to its excellent strength, thermal resistance, and good machinability, making it ideal for aerospace and automotive components.
Aluminum 2014 offers high strength, excellent machinability, good wear resistance, and superior performance under high-stress conditions, making it ideal for aerospace, automotive, and structural custom forgings.
Forged Aluminium 2014 is used extensively in aerospace parts, military hardware, engine mountings, truck frames, structural members, and other heavy loads. It is used where machining complexity and strength are high. Because of its excellent fatigue resistance and strength, 2014 is also used in large aircraft components, heavy truck suspension, and structural frameworks in the construction or defense industries. It is used inside or sheltered areas because of its poor corrosion resistance.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Chung Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Da Nang, Vietnam
Copyright 2024 Chung Metals. All rights reserved