Chung Metal provides Stainless Steel 15-7 MO Bars and Rods in Da Nang, Vietnam, known for excellent strength and oxidation resistance. This precipitation-hardened stainless steel has high fatigue strength and corrosion protection. Chung Metal’s modern production ensures ideal hardness control and surface finish. The 15-7 MO bars retain strength even at high temperatures, offering superior stability and formability. These bars are extensively employed in high-stress mechanical components wherein strength, reliability, and corrosion resistance are critical.
15-7 MO has 15% chromium, 7% nickel, and ~2.5% molybdenum, with aluminum and carbon as aging hardeners. It offers tensile strength up to 1400 MPa, yield 1200 MPa, and hardness ~46 HRC. The alloy has high strength and corrosion resistance after aging.
Dimension : EN, DIN, JIS, ASTM, BS, ASME, AISI
Grade : 15-7MO (UNS No. S15700) Round Bars 1.4532
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Form : Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc.
Surface : Hot Rolled Pickled or Sand Blasting Finished, Cold Drawn, Bright, Polished, Hairline
Application : Chemical process, Food processing, Petrochemical, Pollution control, Pulp and Paper, Refining
Condition : Cold Drawnd Pulished Cold Drawn Centreless Ground & Polished.
Our 15-7MO Round Bars conforms to NACE MR0175/ISO 15156
| Weight% | C | Mn | Si | P | S | Cr | Ni | Mo | Al |
| 15-7Mo | 0.09 | 1 | 1 | 0.04 | 0.03 | 14-16 | 6.50-7.75 | 2-3 | 0.75-1.5 |
| Material | Condition | Thickness (in) | Tensile Strength (ksi) | Yield Strength (ksi) | Elongation % | Hardness |
| Alloy 15-7 Mo | Solution Treated | <0.005 | 150 (max) | 65 (max) | 25 | 100 HB (max) |
| Alloy 15-7Mo | TH1050 (AMS 5520) | 0.010-0.020 | 190 | 170 | 4 | 40 HRC |
| Alloy 15-7 Mo | TH1050 (AMS 5520) | 0.020-0.1875 | 190 | 170 | 5 | 40 HRC |
| Alloy 15-7 Mo | TH1050 (AMS 5520) | 0.1875-0.500 | 190 | 170 | 6 | 40 HRC |
| Alloy 15-7 Mo | RH950 (AMS 5520) | 0.010-0.020 | 225 | 220 | 3 | 45 HRC |
| Alloy 15-7 Mo | RH950 (AMS 5520) | 0.020-0.1875 | 225 | 220 | 4 | 45 HRC |
| Alloy 15-7 Mo | RH950 (AMS 5520) | 0.1875-0.500 | 225 | 220 | 5 | 45 HRC |
| Alloy 15-7 Mo | Condition C | – | 200 | 175 | 1 | 41 HRC |
| Alloy 15-7 Mo | Condition CH900 | – | 240 | 230 | 1 | 46 HRC |
| STANDARD | WERKSTOFF NR. | UNS |
| SS 15-7MO | 1.4532 | S15700 |
Stainless Steel 15-7 MO Bars and Rods are typically heat-treated to achieve optimal strength and hardness. The standard heat treatment involves solution annealing at 1030-1070°C followed by a rapid quenching process to enhance their mechanical properties, such as tensile and yield strength.
Stainless Steel 15-7 MO Bars and Rods generally require minimal maintenance due to their excellent corrosion resistance. Regular cleaning with non-abrasive materials is recommended to maintain their appearance and prevent surface corrosion. For extreme environments, periodic inspections and maintenance are advised to ensure their long-term performance.
15-7 MO bars find application in springs, aerospace hardware, pressure diaphragms, and fasteners. They retain structural integrity in dynamic and thermal stress. Chung Metal’s 15-7 MO rods provide consistent performance for precision components of aircraft and industrial systems.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Chung Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Da Nang, Vietnam